| MANUFACTURING CAPABILITY |
| We offer the following Raw Material, with these heat treatment options |
| GRADE |
TYPE |
PROCESS |
HARDNESS / CASE DEPTH |
| EN31 / SAE52100 / 100Cr6 / SUJ2 |
Ball Bearing Steel |
Through Hardening |
45 -65 HRC with the range of 4 HRC |
| If wall thickness > 7mm 50 - 60 only |
| EN19 |
Chromium Molly Steel |
Thorugh Hardening |
40 - 62 HRC |
| Case Hardening |
40-55 HRC / 1.2 to 3 mm |
| EN24 |
Nickel Chromium Molly Steel |
Through Hardening |
45 -65 HRC with the range of 4 HRC |
| Case Hardening |
40-55 HRC / 1.2 to 3mm |
| SAE8620 / 16MnCr5 / 20MnCr5 |
Alloy Case Hardening Steel |
Case Hardening |
45-62 HRC / 0.25 to 1.00 mm |
| EN353 / EN36 |
45-65 HRC / 0.25 to 1.20 mm |
| EN1A Leaded and Unleaded |
Free Cutting Steel |
Case Hardening / Carbo Nitriding / Carborising |
85 - 90 HRA at 15N / Case Depth 0.08 to 0.25mm |
| EN8 /EN9 |
|
Toughening or Through Hardening |
25 - 33 HRC |
| |
|
|
|
| EN41B |
Nitrinding Steel |
Gas Nitriding for 80 hours heating and 24 hours cooling in furnace |
900 - 1000HV 0.1 / 0.15-0.25mm after grinding of bore and OD with a core hardness of 28- 34 HRC |
| EN47 |
Spring Steel |
Thorugh Hardening |
40-52 HRC |
| CK45 /C45 |
Carbon Steel |
Through Hardening |
32-45 HRC / Case Depth 0.08 to 0.25mm |
| HSS : High Speed Steel |
Alloy Tool Steel |
Thorugh Hardening |
55 - 62 HRC |
| HCHCr |
High Carbon High Chromium Alloy Tool Steel |
Thorugh Hardening |
55 - 62 HRC |
| SS410 |
Corrosion & Heat Resistant Stainless Steel |
Thorugh Hardening |
25 - 28 HRC |
| SS430 |
28 - 32 HRC |
| SS440 |
54 - 58 HRC |
| SS304, SS316 |
|
Soft |
|
| Tungsten Carbide |
NA |
NA |
|